Wrought
iron is being gradually replaced in use by mild rolled steels.
Wrought iron is slightly heavier than cast iron, is a much better
electrical conductor than either cast iron or steel, has a tensile strength
of 40,000 to 60,000 pounds per square inch and costs slightly more than
steel. Unlike either steel or cast iron, wrought iron does not harden when
cooled suddenly from a red heat.
_Grades of Irons._--The mechanical properties of cast iron differ
greatly according to the amount of other materials it contains. The most
important of these contained elements is carbon, which is present to a
degree varying from 2 to 5-1/2 per cent. When iron containing much carbon
is quickly cooled and then broken, the fracture is nearly white in color
and the metal is found to be hard and brittle. When the iron is slowly
cooled and then broken the fracture is gray and the iron is more malleable
and less brittle. If cast iron contains sulphur or phosphorus, it will show
a white fracture regardless of the rapidity of cooling, being brittle and
less desirable for general work.
_Steel._--Steel is composed of extremely minute particles of iron and
carbon, forming a network of layers and bands. This carbon is a smaller
proportion of the metal than found in cast iron, the percentage being from
3/10 to 2-1/2 per cent.
Carbon steel is specified according to the number of "points" of carbon, a
point being one one-hundredth of one per cent of the weight of the steel.